• BACKGROUND
    • Screws and plate are commonly utilized for the fixation of split-type humeral greater tuberosity (GT) fractures. However, the mechanical properties of these 2 types of fixation methods have not been compared directly. The aim of the present study was to evaluate the classic 2 screws fixation with hook locking plate from a mechanical perspective.
  • METHODS
    • Sixteen synthetic humerii (Sawbones Pacific Research Laboratories, Vashon, WA, USA) were divided into 2 groups. An osteotomy was performed to simulate a split-type GT fracture. Group A (n = 8) was fixed with 2 standard parallel screws. Group B (n = 8) was fixed with a hook plate. Each specimen was tested with traction force at 45° shoulder abduction. Following the 20-N preload, a 500-cycle loading test was applied with a force ranging from 20 to 200 N (valley/peak), and the interfragmental displacement was measured periodically at intervals of 100 cycles. Finally, all the specimens were pulled with destructive force at a rate of 5 mm/min until catastrophic failure.
  • RESULTS
    • The hook plate exhibited greater construct stiffness than the screw fixation (63.2 ± 6.1 N/mm vs. 40.9 ± 3.4 N/mm, P < .001). All of the specimens completed the entire cyclic loading test without catastrophic failure, and the fragment displacement after 500 cycles was 0.4 ± 0.2 mm for the hook plate and 2.1 ± 0.3 mm for screw fixation, which was statistically lower in the plate group (P < .001). In terms of failure load, the hook plate group exhibited a significantly greater value than the screw group (770.6 ± 94.6 vs. 427.5 ± 45.1 N/mm, P < .001). The failure modes of both fixation methods were distinct.
  • CONCLUSION
    • In humeral GT fracture fixation, hook plate fixation appears to offer greater construct stiffness and failure load while maintaining fragment stability to resist a physiological traction force. The current study provides support from a mechanical perspective for the clinical application of the hook plate.